Produktdetails:
Die chemische Zusammensetzung und Eigenschaften:
Material |
Chemische Zusammensetzungen (Gew .-%) |
Mechanische Eigenschaften |
|||||
Cu |
Cr |
Gasgehalt |
Härte HB (Mpa) |
Dichte (G / cm³) |
Elektrische Leitfähigkeit (Ms / m) |
||
O |
N |
||||||
CuCr50I |
Balance |
47.1-52.0 |
|
|
80-120 |
≥7,90 |
≥16.0 |
CuCr10C |
Balance |
7,0-12,0 |
|
|
70-100 |
≥8,60 |
≥40,0 |
CuCr25C |
Balance |
24.0-28.0 |
|
|
70-105 |
≥8,30 |
≥28,0 |
CuCr30C |
Balance |
28,1-33,0 |
|
|
75-110 |
≥8,20 |
≥26.0 |
CuCr40C |
Balance |
37,0-42,0 |
|
|
80-120 |
≥8,00 |
≥20,0 |
CuCr40A |
Balance |
37,0-43,0 |
|
|
85-125 |
≥8,00 |
≥20,0 |
CuCr50A |
Balance |
47,0-52,0 |
|
|
85-140 |
≥7,90 |
≥18,0 |
CuCr25P |
Balance |
24.0-28.0 |
≤0.060 |
≤0.0050 |
70-105 |
≥8.10 |
≥28,0 |
CuCr30P |
Balance |
28.1-33.0 |
≤0.065 |
≤0.0050 |
75-110 |
≥7,90 |
≥26.0 |
C-Vakuum-Guss, I-Vakuum-Infiltration, A-Vakuum-Bogenschmelzen, P-Puder-Sintern